铁氧体参数及国内外牌号对照表

HARD FERRITE MAGNETS

Hard ferrite (ceramic) magnets were developed in the 1960's as a low cost alternative to metallic magnets. Even though they exhibit low energy (compared with other permanent magnet materials) and are relatively brittle and hard, ferrite magnets have won wide acceptance due to their good resistance to demagnetization, excellent corrosion resistance and low price per pound. In fact, measured by weight, ferrite represents more than 75 percent of the world magnet consumption. It is the first choice for most types of DC motors, magnetic separators, magnetic resonance imaging and automotive sensors.

Ferrite Magnets characteristics

Mostly Used national standard - SJ285-77 permanent ferrite magnet standard

Chinese SJ/T0410-2000 Permanent Ferrite Manget Standard

In MMPA（0100-87) standard

Ring shape size(mm) D×d×H

NdFeB

Known as third generation of Rare Earth magnets, Neodymium Iron Boron (NdFeB) magnets are the most powerful and advanced commercialized permanent magnet today. Since they are made from Neodymium, one of the most plentiful rare earth elements, and inexpensive iron, NdFeB magnets offer the best value in cost and performance.

NdFeB magnets are available in both sintered and bonded forms. Sintered NdFeB offers the highest magnetic properties (28 MGOe to 50 MGOe) while Bonded NdFeB offers lower energy properties. Although bonded magnets do not possess magnetic properties as advanced as those of sintered magnets, they can be made in shapes and sizes that are difficult to achieve with sintering.

A variety of coatings can be applied to the magnets' surface to overcome the principle drawback of neodymium-based magnets, their tendency to corrode easily.

1.Licensed Products by SSMC-MQ - ISO 9002 Quality Standard Certified

2.The above-mentioned data of magnetic parameters and physical properties are given at room temperature.

3.The maximum service temperature of magnet is changeable due to the ratio length and diameter and enviromental factors.

4.Special properties can be achieved with custom method.

Physical and Mechanical Properties

Max Working Temperature

磁芯参数参看

z变压器基础知识 1、变压器组成： 原边（初级primary side ） 绕组 副边绕组（次级secondary side ） 原边电感（励磁电感）‐‐magnetizing inductance 漏感‐‐‐leakage inductance 副边开路或者短路测量原边 电感分别得励磁电感和漏感 匝数比：K=Np/Ns=V1/V2 2、变压器的构成以及作用： 1）电气隔离 2）储能 3）变压 4）变流 ●高频变压器设计程序： 1.磁芯材料 2.磁芯结构 3.磁芯参数 4.线圈参数 5.组装结构 6.温升校核 1.磁芯材料 软磁铁氧体由于自身的特点在开关电源中应用很广泛。 其优点是电阻率高、交流涡流损耗小，价格便宜，易加 工成各种形状的磁芯。缺点是工作磁通密度低，磁导率 不高，磁致伸缩大，对温度变化比较敏感。选择哪一类 软磁铁氧体材料更能全面满足高频变压器的设计要求， 进行认真考虑，才可以使设计出来的变压器达到比较理 想的性能价格比。 2.磁芯结构 选择磁芯结构时考虑的因数有：降低漏磁和漏感， 增加线圈散热面积，有利于屏蔽，线圈绕线容易，装配 接线方便等。 漏磁和漏感与磁芯结构有直接关系。如果磁芯不需 要气隙，则尽可能采用封闭的环形和方框型结构磁芯。 3.磁芯参数： 磁芯参数设计中，要特别注意工作磁通密度不只是受磁化曲线限制，还要受损耗的限制，同时还与功率传送的工作方式有关。 磁通单方向变化时：ΔB=Bs‐Br，既受饱和磁通密度限制，又更主要是受损耗限制，（损耗引起温升，温升又会影响磁通密度）。工作磁通密度Bm=0.6～0.7ΔB 开气隙可以降低Br,以增大磁通密度变化值ΔB，开气隙后，励磁电流有所增加，但是可以减小磁芯体积。对于磁通双向工作而言： 最大的工作磁通密度Bm，ΔB=2Bm。在双方向变化工作模式时，还要注意由于各种原因造成励磁的正负变化的伏秒面积不相等，而出现直流偏磁问题。可以在磁芯中加一个小气隙，或者在电路设计时加隔直流电容。 4.线圈参数： 线圈参数包括：匝数，导线截面（直径），导线形式，绕组排列和绝缘安排。 导线截面（直径）决定于绕组的电流密度。通常取J为2.5～4A/mm2。导线直径的选择还要考虑趋肤效应。如必要，还要经过变压器温升校核后进行必要的调整。 4.线圈参数： 一般用的绕组排列方式：原绕组靠近磁芯，副绕组反馈绕组逐渐向外排列。下面推荐两种绕组排列形式： 1）如果原绕组电压高（例如220V），副绕组电压低，可以采用副绕组靠近磁芯，接着绕反馈绕组，原绕组在最外层的绕组排列形式，这样有利于原绕组对磁芯的绝缘安排； 2）如果要增加原副绕组之间的耦合，可以采用一半原绕组靠近磁芯，接着绕反馈绕组和副绕组，最外层再绕一半原绕组的排列形式，这样有利于减小漏感。 5.组装结构：

常用铁氧体磁芯规格

常用铁氧体磁芯规格、型号与技术参数来源：中国变压器供应网发布时间：2007-10-20 0:00:00 功率铁氧体磁芯 EI EE EE PQ EC EI60EE80EE35PQ50/50EC90 EI50EE72EE30PQ40/40EC70 EI40EE70EE25PQ35/35EC52 EI35EE60EE19PQ32/30ECI70 EI33EE55EE16PQ32/20EER49/54 EI30EE50EE13PQ26/25EER49/43 EI28EE49EE10PQ26/20EER49/38 EI25EE42—PQ20/20EER42/43 EI22EE42/20—PQ20/16EER42/45 EI19———EER40/45 EI16——UF102EER28L 常用功率铁氧体材料牌号技术参数 项目条件单位PC30PC402500B B253C8N27μi——250023002500230020002000

Bms H=1200A/m mT510510490510450510 Br H=800A/m mT11795100130——Hc—A/m1214.315.915.918.820 Tc —℃>230>215>230>220>200>220 P200mT23℃ 25KHz60℃ 100℃KW/m31306009560090048 —KW/m390—70————KW/m3100—75————100mT60℃ 100KHz100℃ KW/m3—450—450———KW/m3—410—410—— 公司——TDK TDK TOKIN TOKIN FERROC XLUBE SIEMENS EI型磁芯规格及参数 型号A B C D E F H Ae (c㎡) Le (cm) Ve (cm3) AL nH/N2 μe EI1616——512.2—20.198 3.460.6711001575

软磁铁氧体基本磁特性

软磁铁氧体材料和磁心概述 软磁铁氧体材料和磁心概述 软磁铁氧体材料分类 铁氧体又称氧化物磁性材料，它是由铁和其它金属元素组成的复合氧化物。铁氧体采用陶瓷工艺，经高温烧结而制成各种形状的零件。实际上，所有在金属磁性材料中出现的磁现象，在铁氧体中也能观察到，但是有两个基本不同点：一是铁氧体的饱和磁化强度远远低于金属磁性材料，通常为金属材料的一半到五分之一；二是铁氧体的电阻率比金属磁高一百万倍以上。由于这种区别，对于低频（1000 赫兹以下）高功率的磁心一般采用金属磁性材料，用于较高频率（1000 赫兹以上）磁心采用铁氧体材料。按照铁氧体的特性和用途，可把铁氧体分为永磁、软磁、矩磁、旋磁和压磁等五类；如果按照铁氧体的晶格类型来分，最重要的有尖晶石型、石榴石型和磁铅石型等三大类。高频变压器和电器中主要使用软磁铁氧体材料，因此下面主要叙述软磁铁氧体材料的分类及特性。大多数软磁铁氧体属尖晶石结构，一般化学表示式为MeFe 2O 4，这里 Me 表示二价金属元素，如：Mn、Ni、Mg、Cu、Zn等。软磁铁氧体材料是各种铁氧体材料中产量最多，用途最广泛的一种。这类材料的主要特点是起始磁导率高和矫顽力低，即容易磁化也极易退磁，其磁滞回线呈细而长形状。软磁铁氧体材料可按化学成分、磁性能、应用来进行分类。若按化学成分来分类，则主要可分为 MnZn 系、NiZn系和 MgZn 系三大类。MnZn 系铁氧体具有高的起始磁导率，较高的饱和磁感应强度，在无线电中频或低频范围有低的损耗，它是，1兆赫兹以下频段范围磁性能最优良的铁氧体材料。常用的MnZn 系铁氧体，其起始磁导率μi=400～20000，饱和磁感应强度 BS=400～530mT。MnZn 系铁氧体广泛制作开关电源变压器、回扫变压器、宽带变压器、脉冲变压器、抗电磁波干扰滤波电感器及扼流圈等，是软磁铁氧体中产量最大的一种材料（按重量计约占 60%）。NiZn 系铁氧体使用频率 100kHz～100MHz，最高可使用到300MHz。这类材料磁导率较低，电阻率很高，一般为 105～107Ωcm。因此，高频涡流损耗小，是 1MHz 以上高频段磁性能最优良有材料。常用的 NiZn 系材料，磁导率μi=5～1500，广泛用于制作各种高频固定电感器，可调电感器，谐振回路线圈，线性调节线圈抗电磁波干扰线圈等。附加少量 CuO 的 NiCuZn 系材料，最近在表面安装片式电感器中得到广泛应用。NiZn 系材料制成的各类小型磁心产量很大（按数量计），但按重量计的约占软磁铁氧体材料的 10% 左右。MgZn 系铁氧体材料中附加小量 MnO 后制成 MgMnZn系材料，电阻率较高，广泛用于制作各种显象管或显示的偏转线圈磁心，数量很大，产量约占软磁铁氧体材料的30%（按重量计）左右。MgZn 系铁氧体在某些高频电感线圈及天线线圈中也得到应用。

高性能永磁铁氧体行业分析

高性能永磁铁氧体市场现状及未来发展分析
北京汉鼎世纪咨询有限公司 摘要：近年来,电机在汽车、电动工具、家电、电动玩具、办公设备、计算机等领域应 用的不断深入， 高性能的电机用磁瓦的需求不断增加。 中国作为最大的永磁铁氧体材料生产 国家， 有必要对永磁铁氧体的市场现状和未发展做出预测。 本文拟从永磁铁氧体市场的现状 入手，对下游行业的需求做相应预测，进而推导出未来永磁铁氧体市场的需求。 关键字:永磁铁氧体 市场现状 需求预测
一、永磁铁氧体行业概述 永磁铁氧体是以SrO或BaO及Fe为原料，通过陶瓷工艺（预烧、破碎、制粉、 压制成型、烧结和磨加工）制造而成，具有宽磁滞回线、高矫顽力、高剩磁，一 经磁化即能保持恒定磁性的功能性材料。按生产工艺不同，将永磁铁氧体分为烧 结和粘结两种，其中烧结又分为干压成型和湿压成型，粘结分为挤出成型、压制 成型和注射成型。由粘结铁氧体料粉与合成橡胶复合而制成的具有柔软性、弹性 及可扭曲的磁体又被称做橡胶磁。 根据成型时是否外加磁场则分为各向同性永磁 体和各向异性永磁体。 目前永磁铁氧体的生产主要集中在中国、日本等。日本和美国是世界上最早 从事永磁材料研发和生产的国家，新产品的开发能力强，整体技术含量高，但是 随着生产成本过高，加上环保的需要，发达国家的生产正在不断减少，主要以生 产中高档产品为主，而中低档产品的生产逐渐转移到发展中国家。目前，国际上 知名的铁氧体磁性材料生产企业主要有如日本的 TDK、FDK、EPSON、日立金属、 住友特殊等， 欧洲的 PHILIPS、 德国的 VAC、 EPCOS， 美国的 ARNORD、 MAGNEQUENCH 等。目前全球永磁铁氧体产品开发和生产的最高水平当属于日本 TDK，日本 TDK 从 90 年代中期，就能大批量生产 FB6 系列（FB6N、FB6H、FB6B）材料，目前已 能批量生产 FB9（FB9H、FB9B、FB9N） 、FB12 系列产品（磁性能指标接近理论值） ， 高端永磁铁氧体产品大部分由日本厂商占据，FB4 以下系列中低档产品早已不生 产。 进入 21 世纪以来，世界磁性材料行业纷纷向中国或第三世界地区转移，以 中国为代表的发展中国家承接了大部分永磁铁氧体产业转移， 随着应用市场的不 断深入发展， 中国的永磁铁氧体行业近年来发展迅猛， 技术差距与发达国家相比， 变得越来越小。国内部分厂家已经开发出与 TDK 高端产品牌号相对应的产品，其 中横店东磁开发的 DM4350（对应 TDK FB9H 牌号）和 DM4545 (对应 TDK FB9B 牌 号)已经能够量产。江粉磁材 JMP-5、JMP-6（对应 TDK FB6 牌号）和 JMP-7（对 应 TDK FB9 牌号）已经量产，同时江粉磁材正在积极研发 JMP-8（对应 TDK FB12 牌号）系列产品。

中外钢材牌号对照表

GB ASTM BS JIS NF DIN 08F081006040A04S09CK C10 08081008045M10S9CK C10 10F1010040A10XC10 10101010,1012045M10S10C XC10C10,CK10 151********M15S15C XC12C15,CK15 20201020050A20S20C XC18C22,CK22 25251025S25C CK25 30301030060A30S30C XC32 35351035060A35S35C XC38TS C35,CK35 40401040080A40S40C XC38H1 45451045080M46S45C XC45C45,CK45 50501050060A52S50C XC48TS CK53 55551055070M55S55C XC55 60601060080A62S58C XC55C60,CK60 15Mn151016,1115080A17SB46XC1214Mn4 20Mn201021,1022080A20XC18 30Mn301030,1033080A32S30C XC32 40Mn401036,1040080A40S40C40M540Mn4 45Mn451043,1045080A47S45C 50Mn501050,1052030A52S53C XC48 080M50 20Mn220¤1320,1321150M19SMn42020Mn5 30Mn230¤1330150M28SMn433H32M530Mn5 35Mn235¤1335150M36SMn438(H)35M536Mn5 40Mn240¤1340SMn44340M5 45Mn245¤1345SMn44346Mn7 50Mn250¤~55M5 20MnV20MnV6 35SiMn35C En4637MnSi5 42SiMn35C En4646MnSi4 40B TS14B35 45B50B46H 40MnB50B40 45MnB50B44 15Cr15X5115523M15SCr415(H)12C315Cr3 20Cr20X5120527A19SCr420H18C320Cr4 30Cr30X5130530A30SCr43028Cr4 35Cr35X5132530A36SCr430(H)32C434Cr4 40Cr40X5140520M40SCr44042C441Cr4 45Cr45X5145,5147534A99SCr44545C4 38CrSi38XC 12CrMo12XM620C R.B12CD413CrMo44 15CrMo15XM A-387Cr . B1653STC4212CD416CrMo44 STT42 STB42 20CrMo20XM4119,4118CDS12SCT4218CD420CrMo44 CDS110STT42 STB42 25CrMo4125En20A25CD425CrMo4 30CrMo30XM41301717COS110SCM42030CD4 42CrMo4140708A42 42CD442CrMo4 708M40 35CrMo35XM4135708A37SCM335CD434CrMo4 12CrMoV12X M 12Cr1MoV12X1M13CrMoV42 25Cr2Mo1VA25X2M1μ 20CrV20X612022CrV4

磁芯参数表

常用磁芯参数表 【EER磁芯】 ■ 用途：高频开关电源变压器、匹配变压器、扼流变压器等。 【EE磁芯】 ■ 用途：电源转换用变压器及扼流圈、通讯及其他电子设备变压器、滤波器、电感器及扼流圈、脉冲变压器等。

【ETD磁芯】 ■ 用途：电源转换用变压器及扼流圈、通讯及其他电子设备变压器、滤波器。 【EI 磁芯】 ■ 用途：高频开关电源变压器、功率变压器、整流变压器、电压互感器等。 【ET 磁芯】 ■ 用途：滤波变压器 【EFD 磁芯】 ■ 用途：高频开关电源变压器器、整流变压器、开关变压器等。

【UF 磁芯】 ■ 用途：整流变压器、脉冲变压器、扼流变压器、电源变压器等。 【PQ 磁芯】 ■ 用途高频开关电源变压器、整流变压器等。 【RM 磁芯】 ■ 用途：高频开关电源变压器、整流变压器、屏蔽变压器、脉冲变压器、脉冲功率变压器、扼流变压器、滤波变压器。 【EP 磁芯】 ■ 用途：功率变压器、宽频变压器、屏蔽变压器、脉冲变压器等。

【H 磁芯】 ■ 用途：宽带变压器、脉冲变压器、脉冲功率变压器、隔离变压器、滤波变压器、扼流变压器、匹配变压器等。 软磁铁氧体磁芯形状与尺寸标准(一) 软磁铁氧体磁芯形状 软磁铁氧体是软磁铁氧体材料和软磁铁氧体磁芯的总称。软磁铁氧体磁芯是用软磁铁氧体材料制成的元件或零件，或是由软磁铁氧体材料根据不同形式组成的磁路。磁芯的形状基本上由成型（形）模具决定，而成型（形）模具又根据磁芯的形状进行设计与制造。 磁芯按磁力线的路径大致可分两大类；磁芯按具体形状分，有各种各样： 磁芯按磁力线路径分类 磁芯按使用时磁化过程所产生磁力线的路径可分为开路磁芯和闭路磁芯两类。 第一类为开路磁芯。这类磁芯的磁路是开启的（open magnetic circuits），通过磁芯的磁通同时要通过周围空间（气隙）才能形成闭合磁路。开路磁芯的气隙占磁路总长度的相当部分，磁阻很大，磁路中的部分磁通在达到气隙以前就已离开磁芯形成漏磁通。因而，开路磁芯在磁路各个截面上的磁通不相等，这是开路磁芯的特点。由于开路磁芯存在大的气隙，磁路受到退磁场作用，使磁芯的有效磁导率μe比材料的磁导率μi有所降低，降低的程度决定于磁芯的几何形状及尺寸。 开路磁芯有棒形、螺纹形、管形、片形、轴向引线磁芯等等。IEC 1332《软磁铁氧体材料分类》标准中称开路磁芯为OP类磁芯。 第二类磁芯为闭路磁芯。这类磁芯的磁路是闭合的（closed magnetic circuits），或基本上是闭合的。IEC 1332称闭路磁芯为CL类磁芯。磁路完全闭合的磁芯最典型的是环形磁芯。此外，还有双孔磁芯、多孔磁芯等等。

高性能永磁铁氧体市场现状及未来发展分析

高性能永磁铁氧体市场现状及未来发展分析摘要：近年来,电机在汽车、电动工具、家电、电动玩具、办公设备、计算机等领域应用的不断深入，高性能的电机用磁瓦的需求不断增加。中国早已成为最大的永磁铁氧体材料生产国家，有必要对永磁铁氧体的市场现状和未发展做出预测。本文拟从永磁铁氧体市场的现状入手，对下游行业的需求做相应预测，进而推导出未来永磁铁氧体市场的需求。 关键字:永磁铁氧体市场现状需求预测 一、永磁铁氧体行业概述 永磁铁氧体是以SrO或BaO及Fe2O3为原料，通过陶瓷工艺（预烧、破碎、制粉、压制成型、烧结和磨加工）制造而成，具有宽磁滞回线、高矫顽力、高剩磁，一经磁化即能保持恒定磁性的功能性材料。按生产工艺不同，将永磁铁氧体分为烧结和粘结两种，其中烧结又分为干压成型和湿压成型，粘结分为挤出成型、压制成型和注射成型。由粘结铁氧体料粉与合成橡胶复合而制成的具有柔软性、弹性及可扭曲的磁体又被称做橡胶磁。根据成型时是否外加磁场则分为各向同性永磁体和各向异性永磁体。 目前永磁铁氧体的生产主要集中在中国、日本、美国等。日本和美国是世界上最早从事永磁材料研发和生产的国家，新产品的开发能力强，整体技术含量高，但是随着生产成本过高，加上环保的需要，发达国家的生产正在不断减少，主要以生产中高档产品为主，而中低档产品的生产逐渐转移到发展中国家。目前，国际上知名的铁氧体磁性材料生产企业主要有如日本的TDK、FDK、EPSON、日立金属、住友特殊等，欧洲的PHILIPS、德国的VAC、EPCOS，美国的ARNORD、MAGNEQUENCH 等。目前全球永磁铁氧体产品开发和生产的最高水平当属于日本TDK，日本TDK从90年代中期，就能大批量生产FB6系列（FB6N、FB6H、FB6B）材料，目前已能批量生产FB9（FB9H、FB9B、FB9N）、FB12系列产品（磁性能指标接近理论值），高端永磁铁氧体产品大部分由日本厂商占据，FB4以下系列中低档产品早已不生产。 进入21 世纪以来，世界磁性材料行业纷纷向中国或第三世界地区转移，以中国为代表的发展中国家承接了大部分永磁铁氧体产业转移，随着应用市场的不断深入发展，中国的永磁铁氧体行业近年来发展迅猛，技术差距与发达国家相比，变得越来越小。国内部分厂家已经开发出与TDK高端产品牌号相对应的产品，其中横店东磁开发的DM4350（对应TDK FB9H牌号）和DM4545 (对应TDK FB9B牌号)已经能够量产。江粉磁材JPM-5、JPM-6（对应TDK FB6牌号）和JPM-7（对应TDK FB9牌号）已经量产，同时江粉磁材正在积极研发JPM-8（对应TDK FB12牌号）系列产品。 国内重点永磁铁氧体企业与TDK产品牌号对照表

国内外金属材料牌号对照表

国内外金属材料牌号对照表 国内外常用灰铸铁牌号对照 序号国别铸 1 中国— HT350 HT300 HT250 HT200 HT150 HT100 2 日本— FC350 FC300 FC250 FC200 FC150 FC100 3 美国 NO.60 NO.50 NO.45 NO.35 NO.30 NO.20 — 4 前苏联CЧ40 CЧ3 5 CЧ30 CЧ25 CЧ20 CЧ15 CЧ10 5 德国 GG40 GG35 GG30 GG25 GG20 GG15 — 6 意大利— G35 G30 G25 G20 G15 G10 7 法国 FGL400 FGL350 FGL300 FGL250 FGL200 FGL150 — 8 英国— 350 300 250 200 150 100 9 波兰 Z140 Z135 Z130 Z125 Z120 Z115 — 10 印度 FG400 FG350 FG300 FG260 FG200 FG150 — 11 罗马尼亚 FC400 FC350 FC300 FC250 FC200 FC150 — 12 西班牙— FG35 FG30 FG25 FG20 FG15 — 13 比利时 FGG40 FGG35 FGG30 FGG25 FGG20 FGG15 FGG10 14 澳大利亚 T400 T350 T300 T260 T220 T150 — 15 瑞典 O140 O135 O130 O125 O120 O115 O110 16 匈牙利 OV40 OV35 OV30 OV25 OV20 OV15 — 17 保加利亚— Vch35 Vch30 Vch25 Vch20 Vch15 — 国际标准18 — 350 300 250 200 150 100 (ISO) 泛美标准19 FG400 FG350 FG300 FG250 FG200 FG150 FG100 (COPANT) 20 中国台湾—— FC300 FC250 FC200 FC150 FC100 21 荷兰— GG35 GG30 GG25 GG20 GG15 — 22 卢森堡 FGG40 FGG35 FGG30 FGG25 FGG20 FGG15 — 23 奥地利— GG35 GG30 GG25 GG20 GG15 — 国内外常用球墨铸铁牌号对照

中外常用钢材料牌号对照表

常用国内外钢材牌号对照表 中国 美国 日本 德国 英国 法国 前苏联 国际标准化组织 GB AST JIS DIN 、DINEN BS 、BSEN NF 、NFEN ΓOCT ISO 630 品 名 牌号 牌号 牌号 牌号 牌号 牌号 牌号 Q195 Cr.B Cr.C SS330 SPHC SPHD S185 040 A10 S185 S185 CT1K П CTlC П CTl ПC Q215A Cr.C Cr.58 SS 330 SPHC 040 A12 CT2K П—2 CT2C П—2 CT2ПC —2 Q235A Cr.D SS400 SM400A 080A15 CT3K П—2 CT3C П—2 CT3ПC —2 E235B Q235B Cr.D SS400 SM400A S235JR S235JRGl S235JRG2 S235JR S235JRGl S235JRG2 S235JR S235JRGl S235JRG2 CT3K П—3 CT3C П—3 CT3ПC —3 E235B Q255A SS400 SM400A CT4K П—2 CT4C П—2 CT4ПC —2 普 通 碳 素 结 构 钢 Q275 SS490 CT5C П—2 CT5ПC —2 E275A

中国 美国 日本 德国 英国 法国 前苏联 国际标准化组织 GB AST JIS DIN 、DINEN BS 、BSEN NF 、NFEN ΓOCT IS0 630 品 名 牌号 牌号 牌号 牌号 牌号 牌号 牌号 08F 1008 1010 SPHD SPHE 040A10 80K П 10 1010 S10C S12C CKl0 040A12 XCl0 10 C101 15 1015 S15C S17C CKl5 Fe360B 08M15 XCl2 Fe306B 15 C15E4 20 1020 S20C S22C C22 IC22 C22 20 25 1025 S25C S28C C25 IC25 C25 25 C25E4 40 1040 S40C S43C C40 IC40 080M40 C40 40 C40E4 45 1045 S45C S48C C45 IC45 080A47 C45 45 C45E4 50 1050 S50C S53C C50 IC50 080M50 C50 50 C50E4 优 质 碳 素 结 构 钢 15Mn 1019 080A15 15r

最新常用铁氧体磁芯资料

常用铁氧体磁芯资料

PM型磁芯PM CORES 型号尺寸Dimensions(mm) Type A B C D E F PM50 49.15±0.85 39.65±0.65 19.70±0.30 5.50±0.10 26.80±0.40 38.80±0.20 PM62 61.00±1.00 48.0min 25.00±0.70 5.30±0.30 33.80±0.60 48.80±0.50 PM74 74.00 0 57.0min 29.00±1.00 5.40±0.30 41.00±0.80 59.00±0.60 -3.0 PM87 87.00 +2.0 66.5min 31.70±1.50 8.50±0.40 48.40±0.80 70.00±0.80 -3.0 PM114 114.00 0 88.0min 42.00±1.50 5.40±0.40 63.80±0.80 92.50±0.50 -5.0 型号磁芯参数Core parameter 重量LP2 LP3 Type C1 (mm- 1) Ae (mm2) le (mm) Ve (mm3) weight (g/pr.) AL(nH/N2 ±25%) Pc(W) (max) AL(nH/N2 ±25%) Pc(W) (max) PM50 0.227 370 84.0 31000 140 7700 3.1 PM62 0.190 570 109 62000 385 9700 6.2 PM74 0.162 790 128 101000 470 10000 3.5* PM87 0.161 910 146 133000 817 13000 4.0* 13000 2.7* PM114 0.116 1720 200 344000 1886 18000 10.3* 16000 6.9* 注:AL:1kHz,0.5mA,100Ts Pc:25kHz,200mT,100℃ 100kHz,200mT,100℃ EE型磁芯 EE CORES

常规铁氧体产品性能表

常规铁氧体产品性能表永磁铁氧体材料特性 材料牌号 Br Hcb Hcj(BH)max mT KG KA/m KOe KA/m KOe KJ/m3MGOe Y20 320-380 3.2-3.8 135-190 1.70-2.58 140-195 1.76-2.45 18.0-22.0 2.3-2.8 Y25 360-400 3.6-4.0 135-170 1.70-2.14 140-200 1.76-2.51 22.5-28.0 2.8-3.5 Y28 370-400 3.7-4.0 175-210 2.20-2.64 180-220 2.26-2.77 26.0-30.0 3.3-3.8 Y30H-1 380-400 3.8-4.0 230-275 2.89-3.46 235-290 2.95-3.65 27.0-32.5 3.4-4.1 Y30H-2 395-415 3.95-4.15 275-300 3.46-3.77 310-335 3.90-4.21 28.5-32.0 3.5-4.0 Chinese standard Grade Br Hcb Hcj(BH)max mT KG KA/m KOe KA/m KOe KJ/m3MGOe Y10T 200-235 2.0-2.35 125-160 1.57-2.01 210-280 2.64-3.52 6.5-9.5 0.8-1.2 Y20 320-380 3.2-3.8 135-190 1.70-2.38 140-195 1.76-2.45 18.0-22.0 2.3-2.8 Y22H 310-360 3.1-3.6 220-250 2.77-3.14 280-320 3.52-4.02 20.0-24.0 2.5-3.2 Y23 320-370 3.2-3.7 170-190 2.14-2.38 190-230 2.39-2.89 20.0-25.5 2.5-3.2 Y25 360-400 3.6-4.0 135-170 1.70-2.14 140-200 1.76-2.51 22.5-28.0 2.8-3.5 Y26H 360-390 3.6-3.9 220-250 2.77-3.14 225-255 2.83-3.21 23.0-28.0 2.9-3.5 Y27H 370-400 3.7-4.0 205-250 2.58-3.14 210-255 2.64-3.21 25.0-29.0 3.1-3.7 Y30 370-400 3.7-4.0 175-210 2.2-2.64 180-220 2.64-2.77 26.0-30.0 3.3-3.8 Y30BH 380-390 3.8-3.9 223-235 2.80-2.95 231-245 2.90-3.08 27.0-30.0 3.4-3.7 Y30-1 360-400 3.6-4.0 135-170 1.70-2.14 140-200 1.76-2.51 22.5-28.0 2.8-3.5 Y30BH-1 380-400 3.8-4.0 230-275 2.89-3.46 235-290 2.95-3.65 27.0-32.0 3.4-4.0 Y20-2 395-415 3.95-4.15 275-300 3.46-3.77 310-335 3.90-4.21 28.5-32.5 3.5-4.0 Y32 400-420 4.0-4.2 160-190 2.01-2.38 165-195 2.07-2.45 30.0-33.5 3.8-4.2 Y33 410-430 4.1-4.3 220-250 2.77-314 225-255 2.83-3.21 31.5-35.0 4.0-4.4 Y35 400-410 4.00-4.10 175-195 2.20-2.45 180-200 2.26-2.51 30.0-32.0 3.8-4.0 USA standard Material Br Hcb Hcj(BH)max mT KG KA/m KOe KA/m KOe KJ/m3MGOe C1 230 2.3 148 1.86 258 3.5 8.36 1.05 C5 380 3.8 191 2.4 199 2.5 27 3.4 C7 340 3.4 258 3.23 318 4.00 21.9 2.75 C8(C8A) 385 3.85 235 2.95 242 3.05 27.8 3.5 C9 380 3.8 280 3.516 320 4.01 26.4 3.32 C10 400 4.0 288 3.617 280 3.51 30.4 3.82 C11 430 4.3 200 2.512 204 2.56 34.4 4.32 Europe standard The standard from International Electronics Committee (IEC404-8-1) O×100=Y10T=C1 ×300=Y30=C5 O×330=Y30 BH Grade Allowed Value (min/typical) Br Hcb BrHcj(BH)max

常用铁氧体磁芯规格

常用铁氧体磁芯规格、型号与技术参数 功率铁氧体磁芯 EI EE EE PQ EC EI60 EE80 EE35 PQ50/50 EC90 EI50 EE72 EE30 PQ40/40 EC70 EI40 EE70 EE25 PQ35/35 EC52 EI35 EE60 EE19 PQ32/30 ECI70 EI33 EE55 EE16 PQ32/20 EER49/54 EI30 EE50 EE13 PQ26/25 EER49/43 EI28 EE49 EE10 PQ26/20 EER49/38 EI25 EE42 — PQ20/20 EER42/43 EI22 EE42/20 — PQ20/16 EER42/45 EI19 — — — EER40/45 EI16 — — UF102 EER28L 常用功率铁氧体材料牌号技术参数 项目 条件 单位 PC30 PC40 2500B B25 3C8 N27 μi — — 2500 2300 2500 2300 2000 2000 Bms H=1200A/m mT 510 510 490 510 450 510 Br H=800A/m mT 117 95 100 130 — — Hc — A/m 12 14.3 15.9 15.9 18.8 20 Tc — ℃ >230 >215 >230 >220 >200 >220 P 200mT23℃ 25KHz60℃ 100℃ KW/m3 130 600 95 600 900 48 KW/m3 90 — 70 — — — KW/m3 100 — 75 — — — 100mT60℃ 100KHz100℃KW/m3 — 450 — 450 — — KW/m3 — 410 — 410 — — 公司 — — TDK TDK TOKIN TOKIN FERROCXLUB E SIEMENS

Ansoft中常用硅钢及永磁材料牌号说明

Ansoft中常用硅钢及永磁材料牌号说明相信大家在学习ANSOFT过程中对材料的选择可能有有些困惑，本人刚开始时也是的，但经过查阅资料后，得出了一点心得，与大家共同分享。本人是搞电机的，这里只介绍电机中常用的硅钢和永磁体的牌号选择。 一.硅钢 国产牌号ANSOFT中有DW310_35,DW315_50,DW360_50,DW465_50,DW540_50. 我国牌号表示方法： （1）冷轧无取向硅钢带（片） 表示方法：DW+铁损值（在频率为50HZ，波形为正弦的磁感峰值为1.5T的单位重量铁损值。）的 100倍+厚度值的100倍。如DW470-50 表示铁损值为4.7w/kg，厚度为0.5mm的冷轧无取向硅钢， 现新型号表示为50W470。 （2）冷轧取向硅钢带（片） 表示方法：DQ+铁损值（在频率为50HZ，波形为正弦的磁感峰值为1.7T的单位重量铁损值。）的 100倍+厚度值的100倍。有时铁损值后加G表示高磁感。如DQ133-30表示铁损值为1.33，厚度为 0.3mm的冷轧取向硅钢带（片），现新型号表示为30Q133。 （3）热轧硅钢板 热轧硅钢板用DR表示，按硅含量的多少分成低硅钢（含硅量≤2.8%）、高硅钢（含硅量＞2.8%）。表示方法：DR+铁损值（用50HZ反复磁化和按正弦形变化的磁感应强度最大值为1.5T 时 的单位重量铁损值）的100倍+厚度值的100倍。如DR510-50表示铁损值为5.1，厚度为0.5mm 的热 轧硅钢板。家用电器用热轧硅钢薄板的牌号用JDR+铁损值+厚度值来表示，如JDR540-50。 美国牌号有M15_24G,M15_26G,M19_24G,M19_26G,M19_29,M22_24G,M22_26G,M22_29G等等，这些牌号都是美国标准。与国产牌号的对比具体请见附件文档国内外冷轧无取向硅钢牌号对照表.pdf。 另外说明一下，电机用硅钢是各向异性的无取向硅钢，和变压器选用的各向同性取向钢不同。 还有纯铁牌号steel_1008，steel_1010可用， 对于鼠笼铸铝转子可以选用cast_aluminum_75C。 二.永磁体选择 国产牌号 （1）铁氧体永磁体牌号:Y10T,Y15,Y15H,Y20,Y20H等等类似牌号都是的。具体参数请见下图

铁氧体磁芯功率与频率的关系表

表10-15正激变换器拓扑最大可能输出功率 输出功率（W） 磁芯A e(cm2) A w(cm2) A e A w(cm4) 20kHz 24kHz 48kHz 72kHz 96kHz 150kHz 200kHz 250kHz 300kHz 体积(cm3) E型磁芯 Philips 814E250 0.202 0.171 0.035 1.1 1.3 2.7 4.0 5.3 8.3 11.1 13.8 16.6 0.57 813E187 0.225 0.329 0.074 2.4 2.8 5.7 8.5 11.4 17.8 23.7 29.6 35.5 0.89 813E343 0.412 0.359 0.148 4.7 5.7 11.4 17.0 22.7 35.5 47.3 59.2 71.0 1.64 812E250 0.395 0.581 0.229 7.3 8.8 17.6 26.4 35.3 55.1 73.4 91.8 110.2 1.93 782E272 0.577 0.968 0.559 17.9 21.4 42.9 64.3 85.8 134.0 178.7 223.4 268.1 3.79 E375 0.810 1.149 0.931 29.8 35.7 71.5 107.2 143.0 223.4 297.8 372.3 446.7 5.64 E21 1.490 1.213 1.807 57.8 69.4 138.8 208.2 277.6 433.8 578.4 722.9 867.5 11.50 783E608 1.810 1.781 3.224 103.2 123.8 247.6 371.4 495.1 733.7 1031.6 1289.4 1547.3 17.80 783E776 2.330 1.810 4.217 135.0 161.9 323.9 485.8 647.8 1012.2 1349.5 1686.9 2024.3 22.90 E625 2.340 1.370 3.206 102.6 123.1 246.2 369.3 492.4 769.4 1025.9 1282.3 1538.8 20.80 E55 3.530 2.800 9.884 316.3 379.5 759.1 1138.6 1518.2 2372.2 3162.9 3953.6 4744.3 43.50 E75 3.380 2.160 7.301 233.6 280.4 560.7 841.1 1121.4 1752.2 2336.3 2920.3 3504.4 36.00 EC型磁芯 Philips EC35 0.843 0.968 0.816 26.1 31.3 62.7 94.0 125.3 195.8 261.1 326.4 391.7 6.53 EC41 1.210 1.350 1.634 52.3 62.7 125.5 188.2 250.9 392.0 522.7 653.4 784.1 10.80 EC52 1.800 2.130 3.834 122.7 147.2 294.5 441.7 588.9 920.2 1226.9 1533.6 1840.3 18.80 EC70 2.790 4.770 13.308 425.9 511.0 1022.1 1533.1 2044.2 3194.0 4258.7 5323.3 6388.0 41.10 ETD型磁芯 Philips ETD29 0.760 0.903 0.686 22.0 26.4 52.7 79.1 105.4 164.7 219.6 274.5 329.4 5.50 ETD34 0.971 1.220 1.185 37.9 45.5 91.0 136.5 182.0 284.3 379.1 473.8 568.6 7.64 ETD39 1.250 1.740 2.175 69.6 83.5 167.0 250.6 334.1 522.0 696.0 870.0 1044.0 11.50 ETD44 1.740 2.130 3.706 118.6 142.3 284.6 427.0 569.3 889.0 1186.0 1482.5 1779.0 18.00 ETD49 2.110 2.710 5.718 183.0 219.6 439.2 658.7 878.3 1372.3 1829.8 2287.2 2744.7 24.20 152

铁氧体与钕铁硼的区别

钕铁硼与铁氧体的区别，那种应用广泛？？ 一．钕铁硼与铁氧体的区别 钕铁硼的优点是性价比高，具良好的机械特性;不足之处在于居里温度点低，温度特性差，且易于粉化腐蚀，必须通过调整其化学成分和采取表面处理方法使之得以改进，才能达到实际应用的要求。 铁氧体是一种具有铁磁性的金属氧化物。就电特性来说，铁氧体的电阻率比金属、合金磁性材料大得多，而且还有较高的介电性能。铁氧体的磁性能还表现在高频时具有较高的磁导率。因而，铁氧体已成为高频弱电领域用途广泛的非金属磁性材料。 钕铁硼属于第三代稀土永磁材料，具有体积小、重量轻和磁性强的特点，是目前性能价格比最佳的磁体，在磁学界被誉为磁王。高能量密度的优点使钕铁硼永磁材料在现代工业和电子技术中获得了广泛的应用。在裸磁的状态下，磁力可达到3500高斯左右。 铁氧体又称铁淦氧或磁性瓷，属于非金属磁性材料，是磁性的三氧化二铁与其他一种或多种金属氧化物的复合氧化物(或正铁酸盐)。磁力通常为800-1000高斯，常应用于音箱、喇叭等器械。 钕铁硼磁铁和铁氧体磁铁的区别主要有以下几点： 1.铁氧体磁铁性能不如钕铁硼。 2.价格上.铁氧体的要比钕铁硼磁铁便宜很多。 3.钕铁硼磁铁耐温很好，而普通的钕铁硼通常只能80度，超过了这个工作温度就会出现退磁情况。 4.铁氧体稳定性非常好，它本身是氧化物，很稳定，钕铁硼是合金，及其容易氧化、必须做涂层保护。 磁铁是一个统称，铁氧体、钕铁、塑磁硼都是磁铁。 按照磁性强弱程度来区分的话，钕铁硼磁性最强，其次是铁氧体、塑磁最弱，各种材料有自己不同的牌号表。 按照工艺区分，前面2者为烧结工艺，塑磁为注塑工艺。 机械特性来看，塑磁不容易碎，因为成分中有尼龙。其他2个容易缺角碎裂。 按照工作温度来看，铁氧体的工作温度是-40~200度，（高温与低温都会退磁） 钕铁硼的工作温度是80~230度。 塑磁的工作温度是100~180度。

国内外常用钢材标准牌号对照表20200711165902.doc

国内外常用钢材标准牌号对照表 种中国日本美国英国德国法国前苏联类CB JIS AISI 、ASTM BS DIN NF ΓOCT Q235-A · F SS41 A36、A283C Ust37-2 Q235-A SS41A、B Rst37-2 CT2 20 S20C C1020 En2C C22 C20 20 碳35 S35C C1035 En8A C35 XC38 35 素钢 20g SB42 A285、Gr.B A414、Gr.B 1633Gr.B Ast41 A42C 20K 20（管道用）STPG38、42 A106 、A53 st35.4 16Mn S M50B SM22 1633．Gr.1 st52-3 16Γ 低A516 、 合16MnR SPV36 A515、Gr·60、19Mn5 金Gr·70 钢 15MnV HTP57VW A225 、Gr.A A225、Gr.B 40Mn C1036 En15B 40MnA 40Mn5 40Γ 40Cr SCr4 5140 E n18 S117 41Cr4 38C4 40X 12CrMo A335 、P2 A213、Gr.B 3064-660 1501-620 13CrMo44 12CD4 12XM STT42 15CrMo STC42 A387、Gr.B 1653 16CrMo44 15CD4 15XM STB42 35CrMo SCM3 E4132 E4135 En19B 34CD4 35CD4 35XM 高0Cr13 SUS410 410S S41000 X7Cr13 Z6C13 08X13 合金0Cr18Ni9 SUS304 304 S30400 304S15 X5CrNi189 ZCN18.09 08X18H10 钢 0Cr18Ni10Ti SUS321 321 S32100 321S12 321S20 X10CrNiTi189 Z6CNT18.10 08X18H10T 0Cr17Ni12Mo2 SUS316 316 S31600 316S16 X5CrNiMo1810 Z6CND17.13 08X17H13M2