TDS_Pro-fax_SG899_(E39059)
Pro-fax SG899 Polypropylene Impact Copolymer LyondellBasell
Industries 1of1
Copyright?2011-IDES-The Plastics Web?|800-788-4668or307-742-9227|https://www.wendangku.net/doc/0017808658.html,.
The information presented on this datasheet was acquired by IDES from the producer of the material.IDES makes substantial efforts to assure the accuracy of this data.However,IDES assumes no responsibility for the data values and strongly encourages that upon final material selection,data points are validated with the material supplier.Revision History
Document Created: Thursday,November17,2011 Added to Prospector: June,1999
Last Updated: 5/20/2008
Product Description
"Pro-fax"SG899high flow,high impact polypropylene copolymer resin is tailored for use in automotive interior head impact applications.This resin is designed to be run in conventional injection molding equipment using standard polypropylene processing conditions.It is available in pellet form. General
Material Status?Commercial:Active
Availability?North America
Features?Good Colorability
?Good Moldability ?Good Stiffness
?High Flow?High Impact Resistance
Uses?Automotive Interior Parts
Automotive Specifications ?CHRYSLER MS-DB500 CPN3560 Color:100%Color Match ?CHRYSLER MS-DB500 CPN4382 Color:Natural
?FORD WSB-M4D638-A Color:Natural
?FORD WSS-M4D638-B Color:Natural
?TOYOTA TSM5514G-3A
Forms?Pellets
Processing Method?Injection Molding
Physical Nominal Value(English)Nominal Value(SI)Test Method Specific Gravity
--0.900 0.898g/cm3ASTM D792 --0.900g/cm30.900g/cm3ISO1183 Melt Mass-Flow Rate(MFR)(230°C/2.16kg)35g/10min35g/10min ASTM D1238 Mechanical Nominal Value(English)Nominal Value(SI)Test Method Tensile Strength
Yield 23100psi21.4MPa ASTM D638 Yield,73°F(23°C)3190psi22.0MPa ISO527-2 Tensile Elongation
Yield 6.0% 6.0%ASTM D638 Yield,73°F(23°C) 5.0% 5.0%ISO527-2 Flexural Modulus
1%Secant 3155000psi1070MPa ASTM D790A 73°F(23°C)160000psi1100MPa ISO178 Impact Nominal Value(English)Nominal Value(SI)Test Method Charpy Notched Impact Strength ISO179 -40°F(-40°C) 2.6ft·lb/in2 5.5kJ/m2
73°F(23°C)8.1ft·lb/in217kJ/m2
Notched Izod Impact
73°F(23°C) 3.7ft·lb/in200J/m ASTM D256A -40°F(-40°C) 2.1ft·lb/in2 4.4kJ/m2ISO180 73°F(23°C) 5.7ft·lb/in212kJ/m2ISO180 Thermal Nominal Value(English)Nominal Value(SI)Test Method Deflection Temperature Under Load
66psi(0.45MPa),Unannealed216°F102°C ASTM D648 66psi(0.45MPa),Unannealed199°F93.0°C ISO75-2/B 264psi(1.8MPa),Unannealed126°F52.0°C ISO75-2/A Notes
1 Typical properties:these are not to be construed as specifications.
2 2.0in/min(50mm/min)
3 0.039in/min(1.0mm/min)