ASTM D 3884耐磨性,旋转橡胶砂轮法作业指导书
1. 目的
Destination
建立試驗設備之正確操作方法和程式，以確保試驗品質。
The establishment of test equipment for correct operation methods and procedures, to
ensure that the quality of the test.
2. 適用範圍
The scope of application
此方法是用于对材料表面耐磨性进行测定。
This method is used to paint and varnish wear resistance were determined.
3. 權責
Duty and responsibility
實驗室之所有授權人員。
All qualified testers in the Laboratory.
4. 名詞解釋
Noun explanation
磨损
Abrasion
两个相互接触的物体在压力作用下，表面发生弹塑性变形及塑性流动时，使表面破坏的现象。
Two objects in contact each other under the effect of pressure, the surface elastic-plastic deformation and plastic flow occurs, the surface damage of the phenomenon.
磨損週期
Abrasion cycle
在磨損測試中,一次或多次地研磨過材料表面,或材料表面磨過研磨剂而回到研磨起始位置。
In abrasion testing,one or more movements of the abradant across a material surface,or the material surface across the abradant,that permits a return to its starting position.
5. 作業內容
Operation contents
5.1 測試試樣
Test Specimens
試板
Boards
試樣需是100mm×100mm或直徑100mm大小，中心開有一個直徑為6.35mm的孔，厚度大於6.35mm小於12.7mm的板材。
Specimen cost is 100 mm x 100 mm or 100 mm diameter size, center has a diameter of
6.35 mm hole，thickness is greater than 6.35 mm and less than 12.7 mm.
5.2 儀器
Apparatus
5.2.1 研磨旋轉臺試驗機
Abrasion tester
應當使用如圖1所示的裝置：
The device should be used as showen in figure 1:
1.轉台，能以（60±2）r/min的轉速旋轉，並且能將試板定中心安裝在轉台上且牢
固定住。
Turntable, can with (60 + 2) r/min speed rotation, test board centering and can be
installed on the turntable and live on.
2.兩個橡膠輪，橡膠砂輪型號的選擇應經有關方商定。
The choice of two rubber wheel, rubber wheel models should be decided by the
relevant personage.
3.砝碼，能使每個橡膠砂輪上的負數逐漸增加。
Farmar, can make each rubber wheel on the negative increase gradually.
4.計數器，記錄轉台的循環次數。
Counter, record turntable cycles.
5.整新介質，以摩擦圓片的形式存在，用於整新橡膠砂輪。
The resurface media, in the form of friction wafers, used to resurface new rubber wheel.
5.2.2 吸塵裝置
Dust collection device
吸走磨損過程中產生的顆粒。
Suck the wear process of particles。
5.2.3天平
Balance
精確到0.1mg。
Accurate to 0.1 mg.
圖1
5.3 程式
Procedure
5.3.1 準備
Preparation
從供應商送來的試樣應當檢查其”接收態”，須小心執行以防止測試表面被污染(油脂和汗水等)。
The specimen shall be checked in an “as received” condition from the vendor and care must be exercised to prevent contamination (by grease, perspirants, etc.) of the surface to be tested.
將所選擇的橡膠砂輪安裝到各自的凸緣架上，注意不要用手直接觸摩擦面。調節橡膠砂輪上的負載至有關方商定的值。
Install to their choice of rubber wheel flange shelf, be careful not to direct contact friction surface by hand.To adjust the rubber wheel load to the parties have agreed on the value. 將整新介質圓片安裝到轉台上。小心放下摩擦頭使橡膠砂輪放在圓片上。放置好吸塵嘴，調節吸塵嘴的位置使之距離圓片表面約1mm。
The entire new medium wafer installed on the turntable.Carefully put the friction head make the rubber wheel on the wafer.Vacuuming mouth in place, the regulating
vacuuming the position of the mouth of about 1 mm from the surface of the wafer.
將計數器設定為零。
To set the counter to zero.
打開吸塵裝置然後啟動轉台。將橡膠砂輪在整新介質圓片上運轉規定的轉數來整新橡膠砂輪。
Open the suction device and then start the turntable.The rubber wheel in a whole resurface media operation rules on wafer revolution to a whole new rubber wheel.
試樣在（23±2）℃和相對濕度（50±5）%條件下狀態調節至少16h。
The specimen in (23 + 2) ℃ and (50 + 5) % relative humidity under the condition of state regulation at least 16 h.
5.3.2 測試
Test
如果試樣表面不規則時，在測試前要預先預磨50轉，再用不起毛的紙擦淨。
If, when the specimen surface is irregular in advance to advance before the test to grind turned 50, then wipe with lint-free paper.
稱重狀態調節后或已預磨並用不起毛的紙擦淨的試樣，精確到0.1mg，記錄這一質量。
After weighing state regulation or have pre grinding with a lint-free paper wipe specimen, accurate to 0.1 mg, record the quality.
將計數器設定為零，打開吸塵裝置，然後啟動轉台。
Set the counter to zero and open the suction device, and then start the turntable.
經過規定的轉數后，用不起毛的紙將殘留在試樣上的任何疏鬆的磨屑除去，再次稱量試樣並記錄這一質量。檢查試樣是否被磨穿。
After rules of revolution, with a lint-free paper will remain on the specimen of any loose abrasive dust removing, weigh the specimen and record the quality again.Check whether the specimen was worn through.
通過以一定的間隔中斷試驗來更精確地測量磨穿點並計算經過規定轉數的磨擦循環后的平均質量損耗。
Through to interrupt test at regular intervals to more accurately measure the wear out point through regulation of revolution and calculate the friction loss in the circulation after the average quality.
在另外兩塊試樣上重複磨損步驟並記錄結果。
On the other two pieces of specimen repeated wear steps and record the results.
5.3.3 評估
Evaluation
計算所有三塊試樣的平均質量損耗，精確到1mg。
Calculate the average for all three pieces of specimen quality loss, accurate to 1 mg.
計算試樣被磨穿所需的平均轉數。
Calculate the average specimen is worn through the required number of revolutions. 6. 注釋
Notes
對每一塊試樣，用減量法計算經商定的轉數后的質量損耗。
For each piece of specimen, use the decrement method to calculate the agreed quality loss after the revolution.
試樣磨穿后，質量損耗受底材磨損的影響。
specimen after wear out, the quality loss affected by substrate wear.specimen after wear out, the quality loss affected by substrate wear.
7.注意事項
Cautionary notes
整新介質在被使用50轉后不可繼續使用。
The resurface media cannot continue to use after be used turn 50.
在測試每個試樣前以及每運轉500轉后都要以50轉整新橡膠砂輪，使摩擦面剛好呈圓柱形，並且摩擦與側面之間的邊是銳利的，沒有任何彎曲半徑。首次使用前要整新新的橡膠砂輪。
In testing each specimen before and after each running 500 turn to transfer to the new
rubber wheel, with 50 just make the friction surface and cylindrical, and between friction and side edge is sharp, no bending radius.Before first use of the new new rubber wheel.
8. 作業流程
Operation process
1)依據已確認的服務記錄單,確認樣品數量、型號、測試內容；
2)對樣品進行拍照；
3)填寫試驗記錄表；
4)依測試條件執行耐磨性測試；
5)對被檢測部位進行拍照記錄；
6)檢查是否所有檢測部位被記錄；
7)對於檢驗完成後的樣品還原包裝，保留至出具試驗報告後退回客戶。
1)According to has been confirmed the service record sheet to make specimen quantity、
type、test content;
2)Take a picture to the specimen;
3)Fill in test record;
4)According to the test conditions of performing resistance to abrasion test;
5)On the detected part photograph records;
6)Check whether all test site was recorded;
7)For inspection after the completion of the specimen reducing packaging, to issue a test
report and return customer retention.
9. 參考規範
Reference specification
ASTM D 3884 Abrasion Resistance of Textile Fabrics (Rotary platform,Double-Head
Method)
ISO 7784-2:1997 Paints and varnishes-Determination of resistance to abrasion -Rotating abrasive rubber wheel method
GB/T 1768-2006 色漆和清漆耐磨性測定旋轉橡膠砂輪法
橡胶作业指导书
第一部分 橡胶制品作业指导书 文件编号：HSXZ/ZD-2011-01 编制： 审核： 批准： 本文件于二零一一年二月一日制定并实施
目录 封皮 (1) 目录 (2) 一、硫化工艺流程 (3) 二、板式橡胶支座生产工艺流程图 (4) 三、硫化工艺作业指导书 (6) 1 、板式橡胶支座硫化工艺 (6) 2 、橡胶板、胶条硫化工艺... ........ .. (7) 3 、橡胶伸缩缝工艺 (7) 四、硫化温度、时间的控制规定 (8) 五、平板硫化机工作压力的控制规定 (9) 六、炼胶工艺规程 (10) 七、配料操作规程 (11) 八、涂胶粘剂操作规程 (12) 九、板式橡胶支座加劲钢板的裁制流程 (13) 十、板式橡胶支座加劲钢板的裁制规程 (14) 十一、硫化工安全操作规程 (15) 十二、炼胶机安全使用操作规程 (16) 十三、滚筒抛丸机安全操作规程 (17) 十四、炼胶工序安全操作规程 (18) 十五、剪板机安全操作规程 (19) 十六、冲床安全操作规程 (20) 十七、等离子切割机操作规程 (21)
十八、锅炉工安全操作规程 (22) '、硫化工艺流程 （一）1、板式支座生产工艺流程。 （二）2、橡胶板工艺流程 生胶切割、称量-开炼机塑炼胶、配料称量-开炼机轧胶-出片- 快检—硫化成型—修边—成品—检验—入库—待发 以上工序轧胶为关键工序，硫化为特殊工序。时间和温度为炼胶质量控制点，硫化过程中的时间、温度和压力为质量控制点。
精品文档 1、板式橡胶支座生产工艺流程图 备注：★表示特殊过程 ☆表示关键过程 4欢迎下载
三、硫化工艺作业指导书 一）、板式橡胶支座硫化工艺 1、检查硫化机是否运转正常，同时将机台擦拭干净，然后预热模具，达到所需温度，并检查模腔是否干净。 2、检查案秤准确度。 3、操作工根据《硫化工艺卡》裁减胶片及称量胶片，按照程序要求将胶片和涂好胶的钢板依次装入已预热好的模具中，同时将操作工号放入模具内侧，然后加盖上模具板。 4、将装好的模具放入平板硫化机中心对称部位加压硫化。 5、将硫化机平板升降二至三次，以排除模具内的空气，使胶料充满模腔。然后保持规定的恒定压力。 6、硫化时间、温度、压力控制。硫化时间为支座厚度的1.3-1.8 倍（分钟）。温度控制在140C 士3。单位面积合模压力》8MP&注: 硫化时间、压力、温度、根据“硫化工艺卡”实施操作并记录）。 7、硫化机运转正常后将操作工具及其他物品放在车间规定的区域内，不可混放；剩余胶边料在专用容器中存放，以备返炼。 8、制品出模时，严禁用利物撬开，以免损坏制品外观质量，出模后先用细砂布打扫模具一遍，再进行下一模操作。 9、出模后的产品经修边自检，自检合格后放入待检区，由专职质检员进行检验。
旋转滤网安装
广东火电工程总公司
目录 1.施工概况 (3) 2.依据的图纸、文件和标准 (3) 3.作业准备和条件要求 (3) 4.施工工序关键的质量控制点 (4) 5.作业程序内容 (4) 6.作业检查验收应达到的质量技术标准 (5) 7.安全措施 (5) 8.作业人员职责、权限 (5) 9.记录和签证 (6) 10.环保要求 (6) 11.附录 (6) 发文范围：（共4 份）归档夹类：作业指导夹号：12 （N为电子分发） 本版文件于2009年月日开始实施。 批准人：
旋转滤网安装 1. 施工概况 广东汕尾红海湾电厂一期工程3、4号机组2×660MW超超临界燃煤机组的循环水泵房共有4个旋转滤网，型号为：XWC-3000。旋转滤网由下列几部分组成。上部机架由带电动机的行星摆线针轮减速机、拉紧装置、安全保护机构、链轮传动系统和冲洗管系统组装在一起，构成水上部分，安装于水室上部的基础上。滚轮导轨（K型带框架）、工作链条和网板构成水下部分，安装于水室中。旋转滤网的滚轮轨道安装于水室两侧，由调整螺栓固定。 2. 依据的图纸、文件和标准 2.1. 旋转滤网总图FO891S-S0105 2.2. 旋转滤网导轨及二次预埋件图F0891S-S0105 2.3. 循环水泵房平面布置图FO891S-S0103 2.4. 验收标准《电力建设施工及验收技术规范（汽轮机机组篇）》 3. 作业准备和条件要求 3.1. 作业所需机工具 3.1.1. 20t吊车1台，40t/10t门式吊车1台 3.1.2. 5米钢尺一把，精度1mm，经检验合格。 3.1.3. 水准仪一台，水平尺一把，。 3.1. 4. 钢丝刷、刮刀、砂布、手锤等常用工具。 3.1.5. 线锤及琴线100m 3.1.6. 2t手动葫芦4个，1t手动葫芦10个。 3.1.7. φ16钢丝绳15米2条, φ8钢丝绳15米15条、10米15条。3.2. 作业前的准备和条件 3.2.1. 基础已验收合格，混凝土强度已达70%以上。基础具有清晰准确的 中心线，循环水泵房有标高线。 3.3. 作业人员的资格 所有作业人员必须经过培训，持有上岗证书，起重工应有一定工作经验。
旋转滤网技术说明书
XWZ、XKZ、XWC、XKC 系列板框式旋转滤网 技术说明 国家电力公司 南京电力自动化设备总厂 二0C一年十月 目录 一刖言二产品名称与型号三标准与规范四结构与原理主要参数与技术要求安装与试运转运行与维护订货须知
一前言 旋转滤网是火力发电厂地表取水流道中必不可少的的滤水清污设备。它与上游侧的拦污栅配套使用，可以有效地拦截和清除水中的携带的水草、树叶、树枝、鱼虾等污物，以及工农业和城市污水处理等垃圾，保证电厂安全，经济运行。近年来，城市给水、化工、冶金和城市污水处理等工程，也日益采用该设备。 二产品名称与型号 1．产品名称 XW—Z —无框架正面进水旋转滤网 XW—C —无框架侧面进水旋转滤网 XK 有框架正面进水旋转滤网 XK 有框架侧面进水旋转滤网 2．产品型号 采用产品名称汉语拼音字头和网板的名义宽度参数构成。 型号示例：XKZ-3000表示旋转滤网、有框架、正面进水、网板的名义宽度3000mmXWC —3000表示旋转滤网、无框架、侧面进水、网板的名义宽度3000m。 上述型号中，在字母Z和C的后面，无其它字母时，表示网板与网板之间的间隙，采用中心旋转重叠式机械自密封结构的网板。当在字母Z和C的后面，增加字母N时，表示网板与网板之间的间隙，采用圆弧啮合式机械自密封结构的网板。 三、标准与规范 XWZ/C、XKZ/C型系列旋转滤网，按照D—SB88V旋转滤网典型设计》图制造与验收。（华 东电力设计院和河海大学联合设计）。并贯彻，采用下列标准与规范。 板框式旋转滤网GB XXX 灰铸铁分类及技术条件GB976 一般工程用铸造碳钢GB5676
水工建筑物金属结构制造安装及验收规范GBJ201 形状和位置公差检测规定GBl958 钢铁工件涂漆前磷化处理技术条件GB6807 涂料涂复通用技术条件SJ2573 机电产品包装通用技术条件GB2759 四、结构与原理 旋转滤网，按进水方式可分为正面进水(Z)和侧面进水(C)两种型式，其进水方式参见图1 和图2。 旋转滤网按其自身的结构，可分为无框架(w)和有框架(K)两种结构型式分别如图4, 6和 图5，8 所示。 板框式旋转滤网，一般由下列几部分组成。上部机架1，带电动机的行星针轮减速机2， 拉紧装置3 ，安全保护机构4 ，链轮传动系统5和冲洗水管系统6组装在一起，构成水上部分，安装于水室上部的基础上。滚轮导轨(K型带框架)7、工作链条8、网板9和底弧坎10构成水下部分，安装于水室中。无框架旋转滤网的滚轮轨道，安装在水室两侧，由予埋螺栓固定。 有框架旋转滤网，在水室两侧全高度予埋n型定位槽，框架式轨道按米或3米分段组装，插入定位槽内，每段之间用螺栓联接，底弧轨与框架焊接成整体，构成网板运转轨道。有框架旋转滤网的优点是：框架式导轨可以分段吊出水室进行维修，予埋n型定位槽的安装精度较低，侧向密封问题较易解决。其缺点是：框架，导轨耗用钢材多，工艺复杂，造价高，增加了水流阻力。无框架旋转滤网的优缺点与有框架旋转滤网相反。 旋转滤网的传动系统如图3所示。 启动电动机1 ，经减速器2 减速后，通过链轮、链条3、4、5 带动主轴6 和工作链轮7 转动，工作链轮带动工作链条8和网板9运动。如图I和图2所示，水流通过网板时，水流中的脏污物被拦截，随网带向上提升，在旋转到旋网上部时，被冲洗水系统喷嘴喷出的压力的水冲洗，迫使脏污物落入排渣槽内，收集排除。
橡胶制品作业指导书
橡胶制品作业指导书 文件编号：YTDQR5.2-4 编制： 审核： 批准： 天津市亚腾达橡塑制品发展有限公司 2015年1月1日实施
目录 一、橡胶制品生产工艺流程 (2) 二、橡胶制品生产工艺流程图 (2) 三、硫化工艺作业指导书 (3) 四、平板硫化机工作压力的控制规定 (5) 五、橡胶制品检验 (6)
一、橡胶制品生产工艺流程 工艺流程： 生胶切割、称量→开炼机塑炼胶、配料称量→开炼机轧胶→出片→快检→硫化成型→修边→成品→检验→入库 以上工序轧胶为关键工序，硫化为特殊工序。时间和温度为炼胶质量控制点，硫化过程中的时间、温度和压力为质量控制点。 二、橡胶制品生产工艺流程图 备注：★表示特殊过程 ☆表示关键过程
三、硫化工艺作业指导书 （一）、硫化工艺 1、准备：开机前检查硫化机电源、线路、管路等是否安全、完好；开机检查各部件是否运转正常，同时将机台擦拭干净。根据计划和图纸选择模具，擦拭模具，着重内腔检查、擦拭清理工作，然后预热模具，达到所需温度，并检查模腔是否干净。 2、检查案秤准确度。 3、操作工根据《橡胶制品工艺卡》裁减胶片及称量胶片，按照程序要求将定量胶片装入已预热好的模具和注胶槽中，然后加盖上模具顶盖。 4、将装好的模具放入平板硫化机中心对称部位加压注胶或合模。 5、将硫化机平板升降二至三次，以排除模具内的空气，使胶料充满模腔。然后保持规定的恒定压力和温度。 6、硫化时间、温度、压力控制。硫化时间、压力、温度根据“硫化工艺卡”实施操作并记录。 7、硫化机运转正常后将操作工具及其他物品放在车间规定的区域内，不可混放；剩余胶边料在专用容器中存放，以备返炼。 8、制品出模时，严禁用利物撬开，以免损坏制品外观质量，出模后清理模具一遍，再进行下一模操作。 9、出模后的产品经修边自检，自检合格后放入待检区，由专职质检员进行检验。
旋转滤网技术说明书
XWZ、XKZ、XWC、XKC 系列板框式旋转滤网技术说明书 国家电力公司 南京电力自动化设备总厂 二OO一年十月 目录 一前言 二产品名称与型号 三标准与规范 四结构与原理 五主要参数与技术要求 六安装与试运转 七运行与维护 八订货须知
一前言 旋转滤网是火力发电厂地表取水流道中必不可少的的滤水清污设备。它与上游侧的拦污栅配套使用，可以有效地拦截和清除水中的携带的水草、树叶、树枝、鱼虾等污物，以及工农业和城市污水处理等垃圾，保证电厂安全，经济运行。近年来，城市给水、化工、冶金和城市污水处理等工程，也日益采用该设备。 二产品名称与型号 1．产品名称 XWZ——无框架正面进水旋转滤网 XWC——无框架侧面进水旋转滤网 XKZ——有框架正面进水旋转滤网 XKC——有框架侧面进水旋转滤网 2．产品型号 采用产品名称汉语拼音字头和网板的名义宽度参数构成。 型号示例：XKZ—3000表示旋转滤网、有框架、正面进水、网板的名义宽度3000mm；XWC—3000表示旋转滤网、无框架、侧面进水、网板的名义宽度3000mm。 上述型号中，在字母Z和C的后面，无其它字母时，表示网板与网板之间的间隙，采用中心旋转重叠式机械自密封结构的网板。当在字母Z和C的后面，增加字母N时，表示网板与网板之间的间隙，采用圆弧啮合式机械自密封结构的网板。 三、标准与规范 XWZ/C、XKZ/C型系列旋转滤网，按照D—SB88<<旋转滤网典型设计》图制造与验收。(华东电力设计院和河海大学联合设计)。并贯彻，采用下列标准与规范。 板框式旋转滤网GB ╳╳╳ 灰铸铁分类及技术条件GB976 一般工程用铸造碳钢GB5676
砂轮机安全作业指导书(正式)
编订：__________________ 单位：__________________ 时间：__________________ 砂轮机安全作业指导书 (正式) Standardize The Management Mechanism To Make The Personnel In The Organization Operate According To The Established Standards And Reach The Expected Level. Word格式 / 完整 / 可编辑
文件编号：KG-AO-4588-96 砂轮机安全作业指导书(正式) 使用备注：本文档可用在日常工作场景，通过对管理机制、管理原则、管理方法以及管理机构进行设置固定的规范，从而使得组织内人员按照既定标准、规范的要求进行操作，使日常工作或活动达到预期的水平。下载后就可自由编辑。 1 范围 本标准规定了砂轮机安全作业的内容。 本标准适用于砂轮机作业人员安全作业。 2 安全操作要点 2.1 砂轮机应指定人管理、换片，保证其防护装置完整有效。 2.2 必须根据砂轮使用的说明书，选择与砂轮机主轴转数相符合的砂轮。 2.3 新领的砂轮要有出厂质量合格证明文件。安装前如发现砂轮的质量、硬度、粒度和外观有裂缝等缺陷时，不能使用。 2.4 工作前应按要求穿戴好劳动保护用品；确认电源线及防护罩是否安全。 2.5 新装砂轮启动时，先点动检查，经过5～10
分钟试转后，才可使用。 2.6 开动砂轮机前，先检查砂轮机部件是否齐全，必须等砂轮达到额定转速，无振动和其它不良现象后，才可使用。 2.7 禁止磨削紫铜、铅、木头等东西，以防砂轮嵌塞。 2.8 磨削时，人应站在砂轮机的侧面，严禁站在砂轮正面操作，站立位置和姿势必须规范。头部不要靠近砂轮，眼睛要避开火花溅出方向。 2.9 应握牢被磨工件，防止脱落在防护罩内卡破砂轮；加工较小或较轻的工件时，要使用挟持工具，防止伤人。 2.10 初磨时不能用力过猛，以免砂轮受力不均而发生事故。 2.11 不允许在砂轮机上磨削较大较长物体。防止震碎砂轮飞出伤人。 2.12 不允许二人同时使用同一片砂轮，严禁围堆操作。
旋转滤网作业指导书
Q/DTSM×大唐石门发电有限责任公司企业标准 Q/×××××××××—×××× 循环水系统A级检修作业指导书 作业项目：＃旋转滤网检修 作业日期： 批准： 审核： 编制： 2012-12-30修订2013-01-01实施 大唐石门发电有限责任公司发布
目次 1 范围.................................................................................................................................................................... 2 本指导书涉及的资料和图纸............................................................................................................................ 3 安全措施............................................................................................................................................................ 4 备品备件清单.................................................................................................................................................... 5 现场准备及工具................................................................................................................................................ 6 检修工序及质量标准........................................................................................................................................ 7 检修记录............................................................................................................................................................ 8 不符合项目处理单............................................................................................................................................ 9 完工报告单........................................................................................................................................................ 10 质量签证单...................................................................................................................................................... 11质量验评表
砂轮机安全作业指导书通用版
管理制度编号：YTO-FS-PD872 砂轮机安全作业指导书通用版 In Order T o Standardize The Management Of Daily Behavior, The Activities And T asks Are Controlled By The Determined Terms, So As T o Achieve The Effect Of Safe Production And Reduce Hidden Dangers. 标准/ 权威/ 规范/ 实用 Authoritative And Practical Standards
砂轮机安全作业指导书通用版 使用提示：本管理制度文件可用于工作中为规范日常行为与作业运行过程的管理，通过对确定的条款对活动和任务实施控制,使活动和任务在受控状态，从而达到安全生产和减少隐患的效果。文件下载后可定制修改，请根据实际需要进行调整和使用。 1 范围 本标准规定了砂轮机安全作业的内容。 本标准适用于砂轮机作业人员安全作业。 2 安全操作要点 2.1 砂轮机应指定人管理、换片，保证其防护装置完整有效。 2.2 必须根据砂轮使用的说明书，选择与砂轮机主轴转数相符合的砂轮。 2.3 新领的砂轮要有出厂质量合格证明文件。安装前如发现砂轮的质量、硬度、粒度和外观有裂缝等缺陷时，不能使用。 2.4 工作前应按要求穿戴好劳动保护用品；确认电源线及防护罩是否安全。 2.5 新装砂轮启动时，先点动检查，经过5～10分钟试转后，才可使用。 2.6 开动砂轮机前，先检查砂轮机部件是否齐全，必须等砂轮达到额定转速，无振动和其它不良现象后，才可
钢边橡胶止水带作业指导书-
氯丁钢边橡胶止水带完全变形缝作业指导书 氯丁钢边橡胶止水带完全变形缝，是在后浇带等半完全缝形式上发展出来的一种较新型的变形缝模式，氯丁钢边橡胶止水带完全变形缝在防裂缝、防渗漏、抗错位、抗老化等方面较其他半完全缝有很大程度的提高。通过在地区多个污水处理厂工程施工实践，总结形成本作业指导书。 1 特点 1．通过将混凝土结构分割成不同的区块，各区块间仅依靠氯丁钢边橡胶止水带相互柔性连接，可有效地防止混凝土结构出现裂缝和区块间相互位移产生裂隙。 2．橡胶止水带中含氯丁元素，可延长橡胶止水带的使用寿命，确保止水带的使用寿命与混凝土结构使用寿命相吮合。 3．利用钢边与混凝土结构的良好咬合，确保氯丁钢边橡胶止水带与混凝土的良好连接，有效地防止变形缝位置出现渗漏的可能性。 4．施工时确保氯丁钢边橡胶止水带在混凝土结构中的位置是十分重要的，通过与模板安装方式上的有效结合，可达到目的。 2 适用围 适用于各类蓄水构筑物的氯丁钢边橡胶止水带完全变形缝和橡胶止水带变形缝的施工，也可为相应形式的半完全变形缝施工提供参考。 3 工艺原理 通过设置几道变形缝将蓄水池的混凝土结构分断成几个相互独立的部分，相邻独立的池体通过氯丁钢边橡胶止水带嵌入混凝土中进行柔性连接，变形缝座落在氯丁钢边橡胶止水带的正中位置，缝宽为
3~4cm，缝采用聚乙烯泡沫板填充，缝口位置约4cm深度采用双组份聚硫密封膏嵌缝。池的水被氯丁钢边橡胶止水带阻隔在池体部，从而达到不渗漏的目的。 4 工艺流程 池体的底板、墙体、顶板渠道有不同的设计方式，施工工艺流程也有所不同。 底板防渗漏施工工艺流程 墙防渗漏施工工艺流程
5 操作要点 1．混凝土配合比及原材料控制 配合比设计的主导思想是通过外加剂和掺合料的使用来减少混凝土的用水量、降低水灰比、降低混凝土水化热、提高混凝土的自密性。可使用如TW-2型高效防水剂来满足混凝土的减水、防水的目的，掺加粉煤灰来降低水泥用量、提高混凝土自密性、降低混凝土水化热以防止裂缝产生。同时控制混凝土坍落度泵送时控制在120±20mm，非泵送而使用塔吊吊运时混凝土坍落度控制在70-80mm，可有效地保证混凝土的质量。 2．氯丁钢边橡胶止水带变形缝施工 2.1底板变形缝 2.1.1定位测量先在底板垫层上弹出每变形缝中心线位置。 2.1.2缝模板设计安装采用胶合板模板。在变形缝线侧每隔50cm钻一个12mm的孔，往孔中插入12的钢筋头，用铁丝将模板与固定钢筋固定连接。变形缝隙处模板采用18厚胶合板，缝上、下错缝15mm，采用下缝加固采用4*8cm方木，上缝隙采用5*10cm方木加固后贴上一片5mm板，达到上、下平缝的目的，而后用一条5*10方木将上、下两部分连成一整体进行固定。 2.1.3止水带固定 氯丁钢边橡胶止水带的Array固定是通过1.5*4cm的小方木 嵌在止水带的凹槽，将止水带 夹紧，与模板支撑系统形成一
旋转滤网作业指导书
大唐石门发电有限责任公司企业标准 Q/×× ××× ××××—×××× 循环水系统A 级检修作业指导书 作业项目：＃旋转滤网检修 作业日期： 批 准： 审 核： 编 制： 2012-12-30修订 2013-01-01实施 大唐石门发电有限责任公司发布 Q/DTSM ××
目次 1 范围................................................................................. 2 本指导书涉及的资料和图纸............................................................. 3 安全措施............................................................................. 4 备品备件清单......................................................................... 5 现场准备及工具....................................................................... 6 检修工序及质量标准................................................................... 7 检修记录............................................................................. 8 不符合项目处理单..................................................................... 9 完工报告单........................................................................... 10 质量签证单.......................................................................... 11质量验评表
角向砂轮机安全操作规程模板
工作行为规范系列 角向砂轮机安全操作规程（标准、完整、实用、可修改）
编号：FS-QG-37332角向砂轮机安全操作规程 Safety rules for angle grinder 说明：为规范化、制度化和统一化作业行为，使人员管理工作有章可循，提高工作效率和责任感、归属感，特此编写。 1、使用前检查角向砂轮机的各部件是否完好，所有大小零件都需安装正确并符合规定。 2、检查电源线与插头是否完好，不准使用电源线受损的角向砂轮机。 3、角向砂轮机不可弄湿，也不可在潮湿的环境使用。砂轮机手柄应保持干燥，无损坏和裂纹。 4、在工作间隙不使用角向砂轮机或对砂轮机做任何换修的工作时，一定要拔出电源插头。 5、确认角向砂轮机开关已关闭才可插上电源插头。使用后拔出插头，不准握着电源线提起砂轮机。 6、工作时将电源线放置于角向砂轮机的后端。防止电源线被高速旋转的砂轮片损坏而触电。 7、砂轮片拆卸:用专用卡子卡住旋转头的同时用专用工
具逆时针方向旋转砂轮片，即可取出砂轮片。 8、安装砂轮片:安装顺序与拆卸相反，但必须将砂轮片固定牢固。 9、使用角向砂轮机时必须戴防护眼镜。工作时必须紧握砂轮机，并要确保立足稳固。 10、操作角向砂轮机时，火星不能朝着他人或自己。不准在易燃易爆的环境附近使用砂轮机。 11、完工时，一定要将工作场所附近的残留火星扑灭后方可离开。 12、楼梯上作业，必须有专人护住梯子。作业者在楼梯上时应保持身体平衡，用力均匀。 13、高空作业时，拴好安全带，并作好防止角向砂轮机脱落的安全措施。 14、角向砂轮机应定期校验，并粘贴合格证，超过有效期禁止使用。 请输入您公司的名字 Foonshion Design Co., Ltd
循环水泵房旋转滤网安装作业指导书
循环水泵房旋转滤网安装 作业指导书
目录 1. 概况 2. 编制依据 3. 施工准备 4. 施工人员资质要求及职责分工 5. 作业流程 6. 施工过程 7. 质量要求 8. 安全文明施工措施 9. 现场质量计划 发放范围: (共份) 工地总经理□份副总经理（施工）□份副总经理（行政）□份质量部□份行政办□份计划□份技术□份财务□份力特□份合同□份安全□份供应□份锅炉□份机械□份管道□份电仪□份调试□份焊接□份油保□份南管□份质管部□份安监部□份工程策划部□份工程协调部□份 此文件于年月日起实施 批准人
1.概况 XXXX电厂#10机组循环水系统设计两台XWC旋转滤网，用于拦截循环水泵前体积较小的脏物和杂草。滤网布置在循环水泵房循环水泵进口，滤网型式为旋转式，网面呈三角形（V型）结构，其优点：增大滤网有效通流面积，提高清洁能力，减少水阻。网板与网板间设置橡胶密封，网板与导轨间设置了弹性自密封装置，成为全密封结构。传动部分为摆线针轮减速器直联悬挂式蜗轮减速器，其结构紧凑，体积小，传动效率高，主轴受力更趋合理。滤网为中间进水，二侧出水，喷水方式为下喷式，利于脏物的倾倒和洗冲，设备设有过电流保护器，底部导轨较上部宽，以增大进水流量而降低进水流速，保证滤网正常运行。 2．编写依据 2.1设计院提供的安装图纸； 2.2设备厂家提供的图纸及说明书； 2.3《火电施工质量验收及评定标准》（汽机篇）； 2.4《电力施工质量验收及评定标准》（焊接篇） 2.5《电力建设安全工作规程》（火力发电厂部分） 3．施工准备 3.1 施工机具准备 3.1.1链条葫芦2t 4只 3.1.2钢丝绳头若干 3.1.3相关的钳工工具若干 3.2土建准备
砂轮机使用的安全操作规程示范文本
砂轮机使用的安全操作规 程示范文本 In The Actual Work Production Management, In Order To Ensure The Smooth Progress Of The Process, And Consider The Relationship Between Each Link, The Specific Requirements Of Each Link To Achieve Risk Control And Planning 某某管理中心 XX年XX月
砂轮机使用的安全操作规程示范文本使用指引：此操作规程资料应用在实际工作生产管理中为了保障过程顺利推进，同时考虑各个环节之间的关系，每个环节实现的具体要求而进行的风险控制与规划，并将危害降低到最小，文档经过下载可进行自定义修改，请根据实际需求进行调整与使用。 1砂轮机的旋转方向要正确，只能使磨屑向下飞离砂 轮。 2砂轮机启动后，应在砂轮机旋转平稳后再进行磨削。 若砂轮机跳动明显，应及时停机修整。 3砂轮机托架和砂轮之间应保持3mm的距离，以防工 件扎入造成事故。 4磨削时应站在砂轮机的侧面，且用力不宜过大。 5根据砂轮使用的说明书，选择与砂轮机主轴转数相符 合的砂轮。 6新领的砂轮要有出厂合格证，或检查试验标志。安装 前如发现砂轮的质量、硬度、粒度和外观有裂缝等缺陷 时，不能使用。
7安装砂轮时，砂轮的内孔与主轴配合的间隙不宜太紧，应按松动配合的技术要求，一般控制在 0.05?/FONT>0.10毫米之间。 8砂轮两面要装有法兰盘，其直径不得少于砂轮直径的三分之一，砂轮与法兰盘之间应垫好衬垫。 9拧紧螺帽时，要用专用的板手，不能拧得太紧，严禁用硬的东西锤敲，防止砂轮受击碎裂。 10砂轮装好后，要装防护罩，挡板和托架。挡板和托架与砂轮之间的间隙，应保持在1?/FONT>3毫米内，并要略低于砂轮的中心。 11新装砂轮启动时，不要过急，先点动检查，经过5?/FONT>10分钟试转后，才能使用。 12初磨时不能用力过猛，以免砂轮受力不均而发生事故。 13禁止磨削紫铜、铅、木头等东西，以防砂轮嵌塞。
65_90_120橡胶挤出机作业指导书
编号：Q/KH03-01.4-2013 科虹线缆科技股份 作 业 指 导 书 设备名称：冷喂料橡胶挤出机 受控状态： 受控号： 修订装态：A
发布日期：2013年12月10日实施日期：2013年12月10日 目录 一、机器的用途及应用围 二、机器的工艺技术参数 三、机器的结构及简要说明 四、操作与使用 五、工艺过程 六、质量控制要点
七、维护和保养一、机器的用途及应用围
JX-120G型、JX-90型、JX-65型冷喂料橡胶挤出机主要用于电线电缆绝缘护套的挤出包胶，各种胶条、胶带及其他橡胶制品的成型生产。 Ф65连硫挤出机:绝缘和小规格护套. Ф90、Ф90连硫:大规格绝缘及成品护套. 二、机器的工艺技术参数 （一）JX-90型冷喂料橡胶挤出机 1、机头中心高：H=1000mm 2、螺杆外径：D=? 90mm 3、螺杆长径比：L/D=14：1 4、螺杆压缩比：1.42 5、螺杆与机筒间隙（双面）：0.25～0.365mm 6、螺杆转速：4.5～45转/分 7、生产能力：150kg/小时 8、电机型号：YCT315—4A 55KW 132—1320转/分 （二）JX-65型冷喂料橡胶挤出机 1、机头中心高：H=850mm 2、螺杆外径：D=? 65mm 3、螺杆长径比：L/D=12：1 4、螺杆压缩比：1.47 5、螺杆与机筒间隙（双面）：0.205～0.301mm 6、螺杆转速：7～70转/分 7、生产能力：70kg/小时
8、电机型号：YCT250—4A 18.5KW 132—1320转/分 （三）JX-120型冷喂料橡胶挤出机 1、机头中心高：H=1200mm 2、螺杆外径：D=? 120mm 9、螺杆长径比：L/D=14：1 10、螺杆压缩比：1.42 11、螺杆与机筒间隙（双面）：0.25～0.365mm 12、螺杆转速：4.5～45转/分 13、生产能力：500kg/小时 14、电机型号：YCT315—4A 75KW 132—1320转/分 三、机器的结构及简要说明 1、该机主要由机头、左机身、左机身、减速箱、调速电机、电机滑道、电器控制柜等几部分组成。 2、电气安装在电柜，采用集中控制，电机转速由控制器控制，电机输出转距通过减速箱输出轴传给螺杆以达到挤出橡胶的目的。 3、螺杆与减速箱输出轴采用直联式浮动连接，螺杆的轴向力由轴承座的推力轴承来承受，，径向力有一组单列向心球轴承及输出轴来承受，所以具有精度高，传动平稳的特点，螺杆有冷却孔，可用来调节螺杆温度。 4、左右机身及联接法均采用高强度铸钢件，机筒处加工成螺旋槽，使蒸汽及冷却水循环通过，达到均衡调节机身温度的目的。 5、机头采用方型结构，部有蒸汽或冷却水循环槽 6、挤出控温围
旋转滤网作业指导书
实用标准文档 大唐石门发电有限责任公司企业标准 Q/×× ××× ××××—×××× 循环水系统A 级检修作业指导书 作业项目：＃旋转滤网检修 作业日期： 批 准： 审 核： 编 制： 2012-12-30修订 2013-01-01实施 大唐石门发电有限责任公司发布 Q/DTSM ××
目次 1 范围................................................................................. 2 本指导书涉及的资料和图纸............................................................. 3 安全措施............................................................................. 4 备品备件清单......................................................................... 5 现场准备及工具....................................................................... 6 检修工序及质量标准................................................................... 7 检修记录............................................................................. 8 不符合项目处理单..................................................................... 9 完工报告单........................................................................... 10 质量签证单.......................................................................... 11质量验评表
开式水电动旋转滤网
哈密兵团红星2x660MW燃煤发电工程 电动旋转滤网设备 招标文件 招标编号： （第三卷技术规范书） 招标人: 设计单位:西北电力设计院有限公司 二○一六年三月
目录 附件1 技术规范 (1) 1.总则 (1) 2.工程概况...................................... 错误！未定义书签。 3.设计和运行条件 (4) 4.技术条件 (6) 5.质量保证及试验 (8) 6.包装和运输 (9) 7.包装、标志、运输及保管 (10) 8.数据表（投标人可根据所供设备的需要作必要的修改和补充） (13) 9.分包商/外购件情况 (14) 10.大部件情况 (15) 11.差异表 (16) 附件2 供货范围 (2) 1.一般要求 (2) 2.供货范围 (2) 附件3 技术资料和交付进度 (5) 1.一般要求 (5) 2.资料提交的基本要求 (5) 附件4 设备交货进度 (8) 附件5 设备监造（检验）和性能试验 (9) 1.概述 (9) 2.工厂检查 (9) 3.设备监造 (9) 4.性能验收试验 (11) 附件6 技术服务和设计联络 (13) 1.投标方现场技术服务 (13) 2.培训 (14) 3.设计联络会 (14) 附件7 业绩表 (1) 附件8 招标文件附图 (1) 附件9 电气部分技术要求 (3)
附件1 技术规范 1. 总则 1.1本招标文件适用于哈密兵团红星2x660MW燃煤发电工程#1、#2号机组所配套的2台电动选择滤网设备。它提出了该设备的功能设计、结构、性能、安装和试验等方面的技术要求。 1.2本技术规范书提出的是最低限度的技术要求，并未对一切技术细节作出规定，也未充分引述有关标准和规范的条文，投标人应保证提供符合本规范书和最新工业标准的优质产品及其相应服务。 1.3 本技术规范书所引用的标准若与投标人所执行的标准发生矛盾时，按较严格的标准执行。 1.4 在签订合同之后，招标人有权提出因规范标准、规程发生变化和除本技术规范书以外的其他要求而产生的一些补充要求，具体项目由招、投标双方共同商定后，载于本技术规范书。 1.5本技术规范书签字后作为订货合同的技术附件，与定货合同正文具有同等效力。1.6投标人的产品应在600MW超临界及以上容量机组工程有2台机组、2年以上运行业绩，已证明安全可靠。 1.7如投标人所供设备为采用引进技术制造，则应在投标文件中明确说明技术合作方及合作方式。 1.8投标人对真空水泵的成套系统设备（含辅助系统与设备）负有全责，即包括分包（或采购）的产品。分包（或采购）的产品制造商应事先征得招标人的认可。 1.9本工程采用电厂标识系统，编码深度到元件级，投标人提供的技术资料（包括图纸）和设备的标识必须有编码，编码标准符合电厂标识系统编码标准（GB/T 50549-2010）的要求。具体标识要求由设计院在以后的设计联络会上提出。 1.10 若投标人所提供的投标文件前后有不一致的地方，应以更有利于设备安装运行、工程质量为原则，由招标人确定。 1.11 投标人应在投标文件中，对于招标文件进行逐段应答，表明是否接受和同意本招标文件的要求，如：接受和同意招标文件某条款的要求，则在该条款后注明：“理解并承诺完全响应上述条款的要求”；若针对某条款，投标人有特别的建议、方案、技术特点或差异，请在该条款下加以描述和说明。 1.12投标人如对本规范书有偏差(无论多少或微小)都必须清楚地表示在“差异表”中。
砂轮机安全操作规程规范
砂轮机安全操作规程规范 一、使用前准备 1、砂轮机要有专人负责，经常检查，以保证正常运转。 2、更换新砂轮时，应切断总电源，同时安装前应检查砂轮片是否有裂纹，若肉眼不易辨别，可用坚固的线把砂轮吊起，再用一根木头轻轻敲击、静听其声。（金属声则优、哑声则劣）。 3、砂轮机必须有牢固合适的砂轮罩，托架距砂轮不得超过5mm，否则不得使用。 4、安装砂轮时，螺母上的不得过松、过紧，在使用前应检查螺母是否松动。 5、砂轮安装好后，一定要空转试验2～3分钟，看其运转是否平衡，保护装置是否妥善可靠，在测试运转时，应安排两名工作人员，其中一人站在砂轮侧面开动砂轮，如有异常，由另一人在配电柜处立即切断电源。以防发生事故。 6、凡使用者要戴防护镜，不得正对砂轮，而应站在侧面。使用砂轮机时，不准戴手套，严禁使用棉纱等物包裹样品进行磨削。 7、使用前应检查砂轮是否完好（不应有裂痕、裂纹或伤残），砂轮轴是否安装牢固、可靠。砂轮机与防护罩之间有无杂物，是否符合安全要求，确认无问题时，再开动砂轮机。 二、使用中注意事项 1、开动砂轮时必须40～60秒钟转速稳定后方可磨削，磨削刀具时应站在砂轮的侧面，不可正对砂轮，以防砂轮片破碎飞出伤人。 2、在同一块砂轮上，禁止两人同时使用，更不准在砂轮的侧面磨削，磨削时，操作者应站在砂轮机的侧面，不要站在砂轮机的正面，以防砂轮崩裂，发生事故，同时不允许戴手套操作，严禁围堆操作和在磨削时嘻笑与打闹。 3、磨削时的站立位置应与砂轮机成一夹角，且接触压力要均匀，严禁撞击砂轮，以免碎裂，砂轮不得磨笨重的物料或薄铁板以及软质材料(铝、铜等)和木质品。 4、磨样时，操作者应站在砂轮的侧面或斜侧位置，不要站在砂轮的正面，同时样品应略高于砂轮中心位置。不得用力过猛，以防滑脱伤手。 5、砂轮不准沾水，要经常保持干燥，以防湿水后失去平衡，发生事故。 6、不允许在砂轮机上磨削较大较长的物体，防止震碎砂轮飞出伤人。 7、不得单手持工件进行磨削，防止脱落在防护罩内卡破砂轮。 三、使用后注意事项 1、必须经常修整砂轮磨削面，当发现样品严重跳动时，应及时用金刚石笔进行修整。 2、砂轮磨薄，磨小，使用磨损严重时，不准使用，应及时更换，保证安全。 3、磨削完毕，应关闭电源，不要让砂轮机空转，同时要应经常清除防护罩内积尘，并定期检修更换主轴润滑油脂。
涂装作业指导书
涂装作业指导书目的及适用范围 喷涂设备与方法 涂装前表面处理 涂料的成膜方式 漆膜的干燥 涂料品种与特性 涂装病态及防治 油漆返修 安全注意事项 涂装工艺规程
1. 目的及适用范围 为了规范本公司的空气喷涂作业，明确操作及检验注意事项，提高涂装质量，特编制本作业指导书。 适用于本厂喷涂方法。 2. 喷涂设备与方法 2.1 空气喷涂 空气喷涂靠压缩空气的气流使涂料雾化成雾状，在气流的带动下，涂到被涂物表面上。空气喷涂法所使用的设备包括：空气压缩机、油水分离器、供给喷枪漆液的压力供漆桶、喷枪、耐压橡皮管、整套的管接头和管扎头等。 ①空气压缩机 一般应选择能满足2~4支喷漆枪同时工作的耗气量（25~50m3/h）以及气体压力为0.3~0.7MPa（3~7kgf/cm2）的空气压缩机。空气压缩机应定期清洗空气过滤器，转动部位应定期加油，不可自行调节保险阀的限压极限。使用前应先排放空气压缩机出气筒中残余的油和水，以保证喷漆质量。 ②油水分离器 用于洁净压缩空气，保证喷漆质量。注意排放油水分离器中积存的油和水。对滤层至少每隔2~3个月拆开清理一次，经高温烘烤除去油和水后重新使用。 ③压力供漆桶（罐） 用于储存和输送涂料。一般桶压宜在0.1~0.2MPa，桶压应低于喷枪的使用气压，这样才能使压到喷漆口的漆液有充分的雾化机会，从而使漆膜细腻、平滑。 ④喷枪 用于喷涂施工的喷枪有吸上式、重力式和压送式三种。本厂常用吸上式（见图1）喷枪。 吸上式喷枪：原理是利用高速气流而令喷枪局部真空，因而产生吸力把油漆从壶中吸到喷咀加以雾化喷出，主要作大面积喷涂。本厂采用PQ-2型喷枪。 PQ-2型喷漆枪是一种大型喷枪，喷嘴口径Φ1.8~Φ2.1mm，喷嘴与被涂物有效距离260~300mm，喷涂工作压力0.4~0.5MPa，喷出的漆雾面宽可达130~140mm，也可调成直径50mm的圆形。